3M™ Solar Encapsulant Film PO8510
Polyolefin Encapsulant for Photovoltaic Modules

Introduction
3M™ Encapsulant Film PO8510 offers protection against UV aging and weathering – while enabling maximum visible light transmission to solar cells with UV cut-off wavelength350 nm (see graph below).

Features

• Conformable and flexible for ease of lamination

• Durable bonding strength with both glass and backsheet

• Excellent UV and damp-heat stability

• Very low shrinkage rate

• High light transmission

• No acetic acid/No corrosion

• 1/10th MVTR vs. EVA

• Good compatibility with CIGS Modules

• >130°C Creep

• No transmission loss after aging (>1000 hrs)

Typical Physical Properties (data not for specification purposes)

Storage

Shelf life is 6 months under proper storage conditions. The product should be stored indoors with the temperature controlled between 0°C and 30°C and relative humidity below 60%, avoiding direct sunlight. The product should not be placed near any heating equipment or exposed in a dusty place. Check the package box of stored product before unfolding. The product should be used up as soon as possible after the package is unfolded. Any unused product should be properly sealed with original package or similar package.

Suggested Laminating Conditions

Vacuum time and temperature in the laminator are very critical for final properties. Use of thermocouples is suggested to monitor the temperature to achieve the right gel percentage.

DSC and DMA can be used for designing the appropriate lamination cycle if temperature and time are other than the suggested conditionslisted above.

For optimum performance, gel percentage is recommended to be ideally between 70% to 85%.

Contact 3M for additional information.

Precautionary Information

Refer to the product label and Material Safety Data Sheet for health and safety information before using this product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501.

3M™ Solar Encapsulant Film PO8100N
Polyolefin Encapsulant for Photovoltaic Modules

Introduction

3M™ Solar Encapsulant Film PO8100N is a fast cure thermosetting encapsulant designed for high efficiency solar cells in PV modules that enable higher transmission of ultraviolet and visible light to increase module power output(see graph below)

Features

• Conformable and flexible for ease of lamination

• Durable bonding strength with both glass and backsheet

• Excellent UV and damp-heat stability

• Very low shrinkage rate

• High light transmission

• No acetic acid/No corrosion

• 1/10th MVTR vs. EVA

• Good compatibility with CIGS Modules

• >130°C Creep

• No transmission loss after aging(>1000 hrs)

Typical Physical Properties (data not for specification purposes)

Storage

Shelf life is 6 months under proper storage conditions. The product should be stored indoors with the temperature controlled between 0°C and 30°C and relative humidity below 60%, avoiding direct sunlight.The product should not be placed near any heating equipment or exposed in a dusty place. Check the package box of stored product before unfolding. The product should be used up as soon as possible after the package is unfolded. Any unused product should be properly sealed with original package or similar package.

Suggested Laminating Conditions

Vacuum time and temperature in the laminator are very critical for final properties. Use of thermocouples is suggested to monitor the temperature to achieve the right gel percentage.

DSC and DMA can be used for designing the appropriate lamination cycle if temperature and time are other than the suggested conditions listed above. For optimum performance, gel percentage is recommended to be ideally between 70% to 85%.

Contact 3M for additional information.